Fast Model Resin is Formlabs’ fastest resin that is ideal for 3D printing dental models and orthodontic models for thermoforming clear aligners and retainers. Print 11 models on Form 4B in only 9 minutes or 32 models on Form 4BL in 14 minutes.
Fast Model Resin is the next generation of Draft Resin that leverages the Form 4 Series to print three times faster, while offering improved mechanical properties.
| Specification | Value |
|---|---|
| Print Technology | SLA |
| Colours | Grey |
| Applications | Orthodontic Models |
| Compatible Printer | Form 4B, Form 4BL |
| Ultimate Tensile Strength | 62.0 MPa |
| Elongation at Break | 11.0% |
| Flexural Strength | 106.0 MPa |
| Notched Izod | 37.0 J/m |
| Heat Deflection Temp. @ 1.8 MPa | 61.0 °C |
| Heat Deflection Temp. @ 0.45 MPa | 76.0 °C |
| Flexural Modulus | 2740.0 MPa |
| Tensile Modulus | 2670.0 MPa |
Compatibility
Compatible Build Platform: Form 4 Build Platform, Form 4 Flex Build Platform, Form 4L Build Platform, Form 4L Flex Build Platform
Compatible Tank: Form 4 Resin Tank, Form 4L Resin Tank
Compatible Printer: Form 4B, Form 4BL
Why Choose Fast Model Resin?
Fast Model Resin is Formlabs’ fastest dental 3D printing resin, capable of printing at speeds of 100 mm per hour.
Print a Model a Minute
Print 11 arches in one job in just 9 minutes.
Fast Post-Processing
Post-process parts quickly with a 5-minute wash and 5-minute room temperature post-cure.
Unmatched Reliability
Print confidently with an end-to-end product ecosystem rigorously validated for continuous uptime and reliability.
Accurate Orthodontic Models
Consistently create orthodontic models with 95% of printed surface area within 100 μm of the digital model.
What’s New With Fast Model Resin?
Fast Model Resin is the next generation of Draft Resin, formulated to leverage the new Form 4 ecosystem.
Compared to Draft Resin V2, Fast Model Resin is:
- Faster, formulated to take advantage of the new Form 4 ecosystem to print three times faster.
- More opaque and matte in colour.
- Stronger and stiffer, with 45% higher strength and modulus.
Material Properties
Download the Fast Model Resin Technical Data Sheet
| Parameter | Post-cured at room temperature for 5 minutes | Post-cured at 60 °C for 15 minutes |
|---|---|---|
| Ultimate Tensile Strength | 55 MPa | 62 MPa |
| Tensile Modulus | 2500 MPa | 2700 MPa |
| Elongation at Break | 15% | 11% |
| Flexural Strength | 98 MPa | 106 MPa |
| Flexural Modulus | 2600 MPa | 2700 MPa |
| Notched Izod | 30 J/m | 37 J/m |
| Heat Deflection Temperature at 0.45 MPa | 58 °C | 76 °C |
Post-Processing
Wash Settings
Duration: 5 minutes
Start with a 5-minute wash and modify the wash time based on your part geometry and solvent purity.
Cure Settings
Default: 5 minutes at room temperature
Enhanced: 15 minutes at 60 °C
Fast Model Resin can either be used with a 5-minute room temperature cure for faster turnarounds or with a 15-minute cure at 60 °C for improved strength, stiffness, and heat deflection temperature.
Trusted by our customers
See what our customers say about Evo3D
Real feedback from customers who have worked with Evo3D for 3D printers, materials, support and additive manufacturing solutions.
Good experience
“The order was completed but not dispatched for delivery. However, following a call with the company, they immidiately dispatched it with a discount offer for my next purchase. They had reasonable pricing and good customer service. Recommeded.”
Good team, striving to push UK Additive forward
“Olly, Martin, Jake and Martin have all been hugely supportive since our entry into larger scale 3D print last year, and continue to be so. Helpful in their initial advice, supportive since then to help us grow, and as a team they are actively pushing the limits to develop the large format in the UK. And always good to chat to as well!”
Excellent Supplier
“We have been working with Evo3D for about 6 months now and they have been an excellent resource and support to the business I work for. They have worked with us in all sorts of ways to get around any limitations and have supported our projects excellently”